Kobelco DW stainless series MIG wire is less voltage sensitive with less spattering and a higher deposition rate. It has good bead appearance and is easier to do multi-pass welding. CO2 gas is recommended so associated gas costs are lower

• Excellent performance in flat and horizontal position with either 75% argon - 25% Co2 gas mixture or 100% Co2
• Easy slag removal greatly reduces the cleaning time after welding
• Due to less spattering and small spatter size, adhesion of spatter to the base metal is almost eliminated
• Flux-cored wire consists of a tube of 18/8-material filled with a granular core of flux
• The flux contains both slag-forming compounds and alloying elements
• The composition of the flux is important for the welding properties obtained as well as the chemical composition and strength of the weld metal
• 24 - 33 volt
• 210 - 610 in./min. wire feed speed
• 5 - 12 lb/hr deposition rate

Kobelco Premiarc DW316L04528 Stainless Steel Flux-Cored Wire, Gas Shielded, Diameter: .045 Inch, Current Type: DC+, Amperage: 130 - 250 amp, Package: 28 lb Spool, AWS Class: AWS A5.22: E316LT0-1, AWS A5.22: E316LT0-4, Tensile Strength: 81800 psi (100% CO2), Yield Strength: 57521 psi 0.2% (100% CO2), Elongation in 2" (%): 37% (100% CO2), Reduction in Area: 0.36, Welding Process: FCAW (Flux Core)/MIG, Weld Metal Composition: 0.02% Carbon (C), 1.42% Manganese (Mn), 0.47% Silicon (Si), 0.023% Phosphorus (P), 0.013% Sulphur (S), 12.34% Nickel (Ni), 18.68% Chromium (Cr), 2.18% Molybdenum (Mo), 0.014% Nitrogen (N), 7.1% FN